I used CA on my first kit for the herringbone purfling and plastic binding. The cutter had slipped, so I had to add multiple b&w purfling strips and widen the rebate. I sealed the top with one coat shellac taped on all the strips, with gaps getween, then ran ca into the join.

Duco is very hard to find in the UK and I wasnt sure if the Ruderer plastic glue i had would glue the h/bone fibre and the plastic binding, so used ca - it came out real good.

There is also a weldon glue airplane glue is also usable in a pinch. That looks good and if the result works that is perfect. The herringbone will also set with tite bond. Plastic doesn't set will with tite bond.
your binding pics look great

_________________
John Hall
Blues Creek Guitars Inc
Authorized CF Martin Repair Center
Board of Directors of Association of Stringed Instrument Artisans
http://www.bluescreekguitars.com

In my dim dark past, I used UHU 'Hart' glue for tasks that I'd used Duco cement for, and I don't recall seeing much of a difference. Perhaps that is more available in the UK.

_________________
peter havriluk

Thanks guys!

Eleven years after your post I have to ask why duco cement?

KB

_________________
Measure Twice,

Karl B

Hi.

Duco cement gives adequate working time, is clear, and will glue all materials. For instance, titebond won't glue anything but wood or wood byproducts. CA glue will eventually discolor spruce unless the spruce has a finish applied first, plus there's no working time.

I like Duco for rossettes too. It has the best working time for me.

Thank you, I'm going to consider that for my rosette.

_________________
Measure Twice,

Karl B

another point is that it doesn't add water

_________________
John Hall
Blues Creek Guitars Inc
Authorized CF Martin Repair Center
Board of Directors of Association of Stringed Instrument Artisans
http://www.bluescreekguitars.com